PatentDe  


Dokumentenidentifikation EP0671283 09.08.2001
EP-Veröffentlichungsnummer 0671283
Titel Thermotransferbilderzeugungsverfahren
Anmelder Agfa-Gevaert N.V., Mortsel, BE
Erfinder Defieuw, Geert, Septestraat 27, B-2640 Mortsel, BE;
Janssens, Wilhelmus, Septestraat 27, B-2640 Mortsel, BE;
Uytterhoeven, Herman, Septestraat 27, B-2640 Mortsel, BE;
Horsten, Bart, Septestraat 27, B-2640 Mortsel, BE;
Dewanckele, Jean-Marie, Septestraat 27, B-2640 Mortsel, BE;
Van den Bogaert, Jan, Septestraat 27, B-2640 Mortsel, BE
Vertreter derzeit kein Vertreter bestellt
DE-Aktenzeichen 69427635
Vertragsstaaten BE, DE, FR, GB, NL
Sprache des Dokument EN
EP-Anmeldetag 10.03.1994
EP-Aktenzeichen 942006123
EP-Offenlegungsdatum 13.09.1995
EP date of grant 04.07.2001
Veröffentlichungstag im Patentblatt 09.08.2001
IPC-Hauptklasse B41M 5/32
IPC-Nebenklasse B41M 5/38   G03C 1/498   G03C 8/40   

Beschreibung[en]
1. Field of the invention.

The present invention relates to a thermal imaging process, more particularly to a method wherein a thermotransferable reducing agent from a donor element is transferred image-wise to a receiving layer, by means of a thermal head.

2. Background of the invention

Thermal imaging or thermography is a recording process wherein images are generated by the use of imagewise modulated thermal energy.

In thermography two approaches are known :

  • 1. Direct thermal formation of a visible image pattern by imagewise heating of a recording material containing matter that by chemical or physical process changes colour or optical density.
  • 2. Formation of a visible image pattern by transfer of a coloured species from an imagewise heated donor element onto a receptor element.

A survey of "direct thermal" imaging methods is given in the book "Imaging Systems" by Kurt I. Jacobson-Ralph E. Jacobson, The Focal Press - London and New York (1976), Chapter VII under the heading "7.1 Thermography". Thermography is concerned with materials which are not photosensitive, but are heat sensitive. Imagewise applied heat is sufficient to bring about a visible change in a thermosensitive imaging material.

According to a direct thermal embodiment operating by physical change, a recording material is used which contains a coloured support or support coated with a coloured layer which itself is overcoated with an opaque white light reflecting layer that can fuse to clear, transparent state whereby the coloured support is no longer masked. Physical thermographic systems operating with such kind of recording material are described on pages 136 and 137 of the above mentioned book of Kurt I. Jacobson et al.

Yet most of the "direct" thermographic recording materials are of the chemical type. On heating to a certain conversion temperature, an irreversible chemical reaction takes place and a coloured image is produced.

One large group of chemical thermographic systems operates with thermosensitive recording materials wherein two colour forming reactants are present, one of which fuses in the range of 60-120°C and reaches thereby the other reactant. According to another embodiment one of the colour-forming reactants is present in a meltable microcapsule shell or kept separate from the other reactant by a meltable barrier layer that on fusing no longer prevents the direct contact of the colour forming reaction partners.

A wide variety of chemical systems has been suggested some examples of which have been given on pages 138 and 139 of the above mentioned book of Kurt I. Jacobson et al. and by A.S. Diamond, "Specialty papers for thermal imaging", Proceedings of White Papers & Office Automation Conference, MA, 1989.

As colour-forming reactants, a combination of a leucobase and an acid is often used in a direct thermal imaging material. However, the light stability of said leuco dyes is poor and the optical densities obtained with the leucobase system in transmission are low (mostly below 2.0).

It has been suggested to use a thermoreducable silver source in combination with a reducing agent in a direct thermal film in order to increase the optical density in transmission of a printed image (see EP-A-537.975). Although continuous tones can be obtained by said printing method, the gradation produced-by said printing method is too high resulting in only a few intermediate density levels. Fluctuations in the heat transfer from the heat source to the printing material result in a density difference of the final image Thus, it is extremely difficult to obtain images having a uniform density profile. A direct thermal printing method moreover has the disadvantage that in the non-image places the co-reactants always remains unchanged, impairing the shelf-life and preservability.

Thermal dye transfer printing is a recording method wherein a dye-donor element is used that is provided with a dye layer wherefrom dyed portions or incorporated dye is transferred onto a contacting receiving element by the application of heat in a pattern normally controlled by electronic information signals.

In thermal wax printing, the dye layer is transferred to the receiving element, whereas in thermal sublimation printing, also called dye diffusion thermal transfer (D2T2) only the dye is transferred to the receiving element. Thermal wax printing has problems to generate images with continuous tones, while the thermal sublimation printing technique offers only moderate densities in transmission on film (up to 2.5). It has been suggested to increase the density of a print made by thermal sublimation printing by printing several times on the same receiving sheet.

This procedure is slow and optical densities in transmission above 3.0 are hardly obtained with a good image stability.

The above findings illustrate that extreme high densities, which are needed on film for medical purposes, controlling and lowering the gradation to the specific needs requested for special medical diagnostic applications is very difficult to realise in a reproducible manner.

3. Summary of the present invention

It is an object of the present invention to provide a thermal imaging process whereby images are obtained with high optical densities, a low gradation and a good stability.

Further objects will become apparent from the description hereinafter.

According to the present invention, there is provided a thermal imaging process using (i) a donor element comprising on a support a donor layer containing a binder and a thermotransferable reducing agent capable of reducing a silver source to metallic silver upon heating and (ii) a receiving element comprising on a support a receiving layer comprising a silver source capable of being reduced by means of heat in the presence of a reducing agent, said thermal imaging process comprising the steps of

  • bringing said donor layer of said donor element into face to face relationship with said receiving layer of said receiving element,
  • image-wise heating a thus obtained assemblage by means of a thermal head, thereby causing image-wise transfer of an amount of said thermotransferable reducing agent to said receiving element in accordance with the amount of heat supplied by said thermal head,
  • separating said donor element from said receiving element, and subsequent overall heating of said receiving element.

4. Detailed description of the invention

The donor element for use according to present invention comprises on one side of the donor element a donor layer, comprising a reducing agent capable of reducing a silver source to metallic silver upon heating, and a binder.

The reducing agent for the silver source may comprise any of the conventional photographic developers known in the art, such as phenidones, hydroquinones and catechol provided that the reducing agent is thermotransferable.

Examples of suitable reducing agents are aminohydroxycycloalkenone compounds, esters of amino reductones, N-hydroxyurea derivatives, hydrazones of aldehydes and ketones, phosphoramidophenols, phosphoramidoanilines, polyhydroxybenzenes, e.g. hydroquinone, t-butylhydroquinone, isopropylhydroquinone, and (2,5-dihydroxyphenyl)methylsulfone, dihydroxybenzene derivatives such as pyrocatechol, and pyrogallol derivatives such as 4-phenylpyrocatechol, t-butylcatechol, pyrogallol, or pyrogallol derivatives such as pyrogallol ethers or esters, dihydroxybenzoic acid, dihydroxybenzoic acid esters such as dihydroxybenzoic acid, methyl ester, ethyl ester, propyl ester, butyl ester and the like, dihydroxy benzaldehyde and keton derivatives, gallic acid, gallic acid esters such as methyl gallate, ethyl gallate, propyl gallate and the like, gallic acid amides, sulfhydroxamic acids, sulfonamidoanilines, 2-tetrazolylthiohydroquinones, e.g., 2-methyl5-(1-phenyl-5-tetrazolylthio)hydroquinone, , tetrahydroquinoxalines, e.g. 1,2,3,4-tetrahydroquinoxaline, amidoximes, azines, hydroxamic acids, 5-pyrazolones, sulfonamidophenol reducing agents, 2-phenylindan-1,3-dione and the like, 1,4-dihydropyridines, such as 2,6-dimethoxy-3,5-dicarbethoxy-1,4-dihydropyridine, bisphenols, e.g., bis (2-hydroxy-3-t-butyl-5-methylphenyl) methane, bis (6-hydroxy-m-toly)mesitol, 2,2-bis (4-hydroxy-3-methylphenyl)propane, 4,4-ethylidene-bis(2-t-butyl-6-methylphenol) and 2,2-bis (3, 5-dimethyl-4-hydroxyphenyl) propane, ascorbic acid derivatives and 3-pyrazolidones.

Reducing agents derived from dihydroxy or trihydroxyphenyl compounds are especially preferred. Highly preferred are 4-phenyl pyrocatechol and propyl gallate.

As a binder for the donor layer, hydrophilic or hydrophobic binders can be used, although the use of hydrophobic binders is preferred.

Hydrophilic binders which can be used are polyvinylalcohol, gelatine, polyacrylamide and hydrophilic cellulosic binders such as hydroxyethyl cellulose, hydroxypropyl cellulose and the like.

The hydrophobic binders may be used as a dispersion in e.g. water or as a solution in an organic solvent.

Suitable binders for the donor layer are cellulose derivatives, such as ethyl cellulose, methyl cellulose, cellulose nitrate, cellulose acetate formate, cellulose acetate hydrogen phthalate, cellulose acetate, cellulose acetate propionate, cellulose acetate butyrate, cellulose acetate pentanoate, cellulose acetate benzoate, cellulose triacetate; vinyl-type resins and derivatives, such as polyvinyl acetate, polyvinyl butyral, copolyvinyl butyral-vinyl acetal-vinyl alcohol, polyvinyl pyrrolidone, polyvinyl acetoacetal, polyacrylamide; polymers and copolymers derivated from acrylates and acrylate derivatives, such as polymethyl methacrylate and styrene-acrylate copolymers; polyester resins; polycarbonates; copoly(styrene-co-acrylonitrile); polysulfones; polyphenylene oxide; organosilicones, such as polysiloxanes; epoxy resins and natural resins, such as gum arabic. Preferably, the binder for the donor layer of the present invention comprises poly(styrene-co-acrylonitrile) or a mixture of poly (styrene-co-acrylonitrile) and a toluenesulphonamide condensation product.

The binder for the donor layer preferably comprises a copolymer comprising styrene units and acrylonitrile units, preferentially at least 60% by weight of styrene units and at least 25% by weight of acrylonitrile units binder. The binder copolymer may compriser other comonomers than styrene units and acrylonitrile units. Suitable other comonomers are e.g. butadiene, butyl acrylate, and methyl methacrylate. The binder copolymer preferably has a glass transition temperature of at least 50°C.

It is also possible to use a mixture of the copolymer comprising styrene units and at least 15% by weight of acrylonitrile units with another binder known in the art, but preferably the acrylonitrile copolymer is present in an amount of at least 50% by weight of the total amount of binder.

The donor layer generally has a thickness of about 0.2 to 5.0 µm, preferably 0.4 to 2.0 µm, and the amount ratio of reducing agent to binder generally ranges from 9:1 to 1:3 by weight, preferably from 3:1 to 1:2 by weight.

The donor layer may also contain other additives such as i.a. thermal solvents, stabilizers, curing agents, preservatives, dispersing agents, antistatic agents, defoaming agents, and viscosity-controlling agents.

Any material can be used as the support for the donor element provided it is dimensionally stable and capable of withstanding the temperatures involved, up to 400°C over a period of up to 20 msec, and is yet thin enough to transmit heat applied on one side through to the reducing agent on the other side to effect transfer to the receiver sheet within such short periods, typically from 1 to 10 msec. Such materials include polyesters such as polyethylene terephthalate, polyamides, polyacrylates, polycarbonates, cellulose esters, fluorinated polymers, polyethers, polyacetals, polyolefins, polyimides, glassine paper and condenser paper. Preference is given to a support comprising polyethylene terephthalate. In general, suitable supports can have a thickness of 2 to 30 µm, preferably a thickness of 4 to 10µm is used. The support may also be coated with an adhesive or subbing layer, if desired.

Subbing layers comprising aromatic copolyesters, vinylidene chloride copolymers, organic titanate, zirconates and silanes, polyester urethanes and the like can be used.

The donor layer of the donor element can be coated on the support or printed thereon by a printing technique such as a gravure process.

A barrier layer for the reducing agent comprising a hydrophilic polymer may also be employed between the support and the donor layer of the donor element to enhance they transfer of reducing agent by preventing wrong-way transfer of reducing agent backwards to the support. The barrier layer for the reducing agent may contain any hydrophilic material that is useful for the intended purpose. In general, good results can be obtained with gelatin, polyacrylamide, polyisopropyl acrylamide, butyl methacrylate-grafted gelatin, ethyl methacrylate-grafted gelatin, ethyl acrylate-grafted gelatin, cellulose monoacetate, methylcellulose, polyvinyl alcohol, polyethyleneimine, polyacrylic acid, a mixture of polyvinyl alcohol and polyvinyl acetate, a mixture of polyvinyl alcohol and polyacrylic acid, or a mixture of cellulose monoacetate and polyacrylic acid.

Certain hydrophilic polymers e.g. those described in EP 227,091 also have an adequate adhesion to the support and the donor layer, so that the need for a separate adhesive or subbing layer is avoided. The particular hydrophilic polymers used in a single layer in the donor element thus perform a dual function, hence are referred to as barrier/subbing layers.

Owing to the fact that the thin support softens when heated during the printing operation and then sticks to the thermal printing head, thereby causing malfunction of the printing apparatus and reduction in image quality, the back of the support (the side opposite to that carrying the donor layer) is typically provided with a heat-resistant layer to facilitate passage of the donor element past the thermal printing head. An adhesive layer may be provided between the support and the heat-resistant layer.

Any heat-resistant layer known in the field of thermal sublimation printing or wax printing can be used in the present invention.

The heat-resistant layer generally comprises a lubricant and a binder. In the conventional heat-resistant layers the binder is either a cured binder as described in e.g. EP 153,880, EP 194,106, EP 314,348, EP 329,117, JP 60/151,096, JP 60/229,787, JP 60/229,792, JP 60/229,795, JP 62/48,589, JP 62/212,192, JP 62/259,889, JP 01/5884, JP 01/56,587, and JP 92/128,899 or a polymeric thermoplast as described in e.g. EP 267,469, JP 58/187,396, JP 63/191,678, JP 63/191,679, JP 01/234,292, and JP 02/70, 485. During printing, a smooth transport of the donor ribbon and the receiving element is required in order to obtain a good density uniformity all over the print.

It is preferred to use different types of lubricants to allow continuous transport of the donor ribbon relative to the thermal head.

Well known lubricants are polysiloxanes such as those mentioned in EP 267,469, US 4,738,950, US 4,866,028, US 4,753,920 and US 4,782,041. Especially useful slipping agents are polysiloxane-polyether block or graft polymers.

Other lubricants for the heat-resistant slipping layer of the donor element are phosphoric acid derivatives such as those mentioned in EP 153,880 and EP 194,106, metal salts of long fatty acids (such as mentioned in EP 458,538, EP 458,522, EP 314, 348, JP 01/241,491 and JP 01/222,993), wax compounds such as polyolefin waxes such as e.g. polyethylene or polypropylene wax, carnauba wax, candelilla wax, bees wax, glycerine monostearate, amid wax such as ethylene bisstearamide and the like.

A heat-resistant layer such as mentioned in EP-A 634 291 is especially preferred.

Inorganic particles such as salts derived from silica such as e.g. talc, clay, china clay, mica, chlorite, silica, or carbonates such as calcium carbonate, magnesium carbonate or calcium magnesium carbonate (dolomite) can be further added to the heat-resistant layer.

It is highly preferred to add mixtures of particles to the heat resistant layer having a Mohs hardness below 2.7 and particles having a Mohs hardness above 2.7 such as mentioned in EP-A 628 428.

A mixture of talc and dolomite particles is highly preferred.

A particular heat-resistant layer for the present invention comprises as a binder a polycarbonate derived from a bis-(hydroxyphenyl)-cycloalkane, corresponding to general formula (I) :

wherein :
  • R1, R2, R3, and R4 each independently represents hydrogen, halogen, a C1-C8 alkyl group, a substituted C1-C8 alkyl group, a C5-C6 cycloalkyl group, a substituted C5-C6 cycloalkyl group, a C6-C10 aryl group, a substituted C6-C10 aryl group, a C7-C12 aralkyl group, or a substituted C7-C12 aralkyl group; and
  • X represents the atoms necessary to complete a 5- to 8-membered alicyclic ring, optionally substituted with a C1-C6 alkyl group, a 5-or 6-membered cycloalkyl group or a fused-on 5- or 6-membered cycloalkyl group,
as lubricants polyether modified polysiloxane block copolymer and zinc stearate and as particles talc particles with a weight average particle size of 4.5 µm.

Lubricants and binder can be coated in a single layer, or can be casted in a separate layer. It is highly preferred to cast the salt of a fatty acid in the heat resistant layer (e.g. as a dispersion) and the polysiloxane based lubricant in a separate topcoat. This separate topcoat is preferably casted from a non-solvent for the heat-resistant layer.

The heat-resistant layer of the donor element may be coated on the support or printed thereon by a printing technique such as a gravure printing.

The heat-resistant layer thus formed has a thickness of about 0.1 to 3 µm, preferably 0.3 to 1.5 µm.

Preferably a subbing layer is provided between the support and the heat-resistant layer to promote the adhesion between the support and the heat-resistant layer. As subbing layer any of the subbing layers known in the art for dye-donor elements can be used. Suitable binders that can be used for the subbing layer can be chosen from the classes of polyester resins, polyurethane resins, polyester urethane resins, modified dextrans, modified cellulose, and copolymers comprising recurring units such as i.a. vinyl chloride, vinylidene chloride, vinyl acetate, acrylonitrile, methacrylate, acrylate, butadiene, and styrene (e.g. poly(vinylidene chloride-co-acrylonitrile). Suitable subbing layers have been described in e.g. EP 138,483, EP 227,090, EP-A 564 010, US 4,567,113, US 4,572,860, US 4,717,711, US 4,559,273, US 4,695,288, US 4,727,057, US 4,737,486, US 4,965,239, US 4,753,921, US 4,895,830, US 4,929,592, US 4,748,150, US 4,965,238, and US 4,965,241.

The receiving element for use according to the printing method of the present invention comprises a receiving layer provided on a support, said receiving layer comprising a silver source capable of being reduced by means of heat in the presence of a reducing agent.

The reducible silver source may comprise any material which contains a reducible source of silver ions. Silver salts of organic and hetero-organic acids, particularly long chain fatty carboxylic acids (comprising from 10 to 30, preferably 15 to 25 carbon atoms) are preferred. Complexes of organic or inorganic silver salts in which the ligand has a gross stability constant for silver ion of between 4.0 and 10.0 are also useful. Examples of suitable silver salts are disclosed in Research Disclosure Nos. 17029 and 29963 and include : salts of organic acids, e.g., gallic acid, oxalic acid, behenic acid, stearic acid, palmitic acid, lauric acid and the like; silver carboxyalkylthiourea salts, e.g., 1-(3-carboxypropyl)thiourea, 1-(3-carboxypropyl)-3,3-dimethylthiourea and the like; complexes of silver with the polymeric reaction product of an aldehyde with a hydroxy-substituted aromatic carboxylic acid, e.g., aldehydes, such as formaldehyde, acetaldehyde and butyraldehyde, and hydroxy-substituted acids, such as salicyclic acid, benzilic acid, 3,5-dihdyroxybenzilic acid and 5,5-thiodisalicylic acid; silver salts or complexes of thiones, e.g., 3-(2-carboxyethyl)-4-hydroxymethyl-4-thiazoline-2-thione and 3-carboxymethyl-4-methyl-4-thiazoline-2-thione; complexes of salts of silver with nitrogen acids selected from imidazole, pyrazole, urazole, 1,2,4-triazole and 1H-tetrazole, 3-amino-5-benzylthio-1,2,4-triazole and benzotriazole; silver salts of saccharin, 5-chlorosalicylaldoxime and the like; and silver salts of mercaptides.

The preferred silver source is silver behenate.

The silver source is preferably added as a dispersion to the coating liquid of the receiving layer.

As binding agent for the receiving layer preferably thermoplastic water insoluble resins are used wherein the ingredients can be dispersed homogeneously or form therewith a solid-state solution. For that purpose all kinds of natural, modified natural or synthetic resins may be used, e.g. cellulose derivatives such as ethylcellulose, cellulose esters, carboxymethylcellulose, starch ethers, polymers derived from α,β-ethylenically unsatured compounds such as polyvinyl chloride, after chlorinated polyvinyl chloride, copolymers of vinyl chloride and vinylidene chloride, copolymers of vinyl chloride and vinyl acetate, polyvinyl acetate and partially hydrolysed polyvinyl acetate, polyvinyl alcohol, polyvinyl acetals, e.g. polyvinyl butyral, copolymers of acrylonitrile and acrylamide, polyacrylic acid esters, polymethacrylic acid esters and polyethylene or mixtures thereof. A particularly suitable ecologically interesting (halogen-free) binder is polyvinyl butyral. A polyvinyl butyral containing some vinyl alcohol units is marketed under the trade name Butvar™ B79 of Monsanto USA.

The binder to organic silver salt weight ratio is preferably in the range of 0.2 to 6, and the thickness of the image forming layer is preferably in the range of 5 to 16 µm.

It is preferred to use a so-called toning agent in the receiving layer or in a layer adjacent to said receiving layer. This toning agent serves to change the tone of the silver image from brown to black or grey. Suitable toning agents are e.g. phthalazinone, phthalazine, phthalimide, succinimide, phthalic acid, benzimidazole or a compound according to formula (II) :

The use of phthalazinone or compound (II) is highly preferred.

It is highly preferred to use a release agent in the receiving element on the side of the receiving layer. This release agent may be added to the coating solution of the receiving layer or may be applied, optionally in a mixture with other ingredients, as a separate layer called the release layer on top of said receiving layer. The use of a release layer is preferred, since the release agent is in that case on top of the receiving element.

The use of a release agent is preferred in the printing method of the present invention since the reducing agents useful in the present invention can give rise to a sticky contact between donor element and receiving element.

As release agents, inorganic and organic release agents can be used. Among them, the organic release agents are preferred.

Solid waxes, fluorine- or phosphate-containing surfactants and silicone oils can be used as releasing agent. Suitable releasing agents have been described in e.g. EP 133012, JP 85/19138, and EP 227092.

When, as mentioned above, a separate release layer, incorporating the release agent, is coated on top of said receiving layer, other ingredients such as binders, plasticizers, or particulate fillers such as talc, silica or collodial particles can be added to said release layer, provided that the transfer of the reducing agent to the receiving layer comprising the reducible silver source can take place.

Examples of binders for the release layer are polyvinylbutyral, ethylcellulose, cellulose acetate propionate, cellulose acetate butyrate, polyvinylchloride, copolymers of vinylchloride, vinylacetate and vinylalcohol, aromatic or aliphatic copolyesters, polymethylmethacrylate, polycarbonates derived from bisphenol A, polycarbonates comprising bisphenols according to formula (I) and the like. The release layer can also act as a protective layer for the images.

A subbing layer is usually provided between the support and the receiving layer, such as those mentioned in e.g. US 4,748,150, US 4,954,241, US 4,965,239 and US 4,965,238 and EP-A 574 055.

The subbing layer can further comprise other polymers, particles, or low molecular weight additives. Addition of inorganic particles such as silica, colloidal silica, water soluble polymers such as gelatin, polymeric latices, polystyrene sulfonic acid and polystyrene sulfonic acid sodium salt, surfactants such as cationic, anionic, amphoteric and non-ionic surfactants, and polymeric dispersants is preferred.

Especially preferred additives are colloidal silica, the above mentioned surfactants, butadiene containing latices such as poly(butadiene-co-methylmethacrylate-co-itaconic acid), polystyrene sulfonic acid and polystyrene sulfonic acid sodium salt. The addition of silica to the subbing layer decreases sticking on the coating roll after coating of the subbing layer. The addition of polystyrene sulfonic acid or polystyrene sulfonic acid sodium salt to the subbing layer accelerates the recycling process.

The subbing layer of the present invention is applied directly to the support of the receiving element. The subbing layer can be applied by coextrusion or can be coated on the support. Coating from an aqueous solution is preferred due to its simplicity and the possibility of adding other ingredients.

The receiving layer is usually hydrophobic in order to enhance the absorption of reducing agent into the receiving element. The polyester recycling procedure, however, uses a cleaning step whereby the film waste is immersed in an alkaline or acid soap solution in water. It is an object of this cleaning process to remove all layers casted on the polymeric substrate.

In order to remove the hydrophobic receiving layer, it is highly preferred to cast- an intermediate layer of an hydrophilic polymer between the subbing layer and the receiving layer. This intermediate layer accelerates the cleaning step in the recycling procedure. Typical examples of hydrophilic polymers which can be used in such intermediate layers are polyvinyl alcohol, polyacrylamide, hydroxyethylcellulose, gelatin, polystyrene sulfonic acid, polyethylene glycol, poly(meth)acrylic acid, poly(meth)acrylic acid, alkali metal salts of polyacrylic acid, crosslinked copolymers containing (meth)acrylic acid or alkali metal salts of (meth)acrylic acid, alkali metal salts of polystyrene sulfonic acid, dextran, carrageenin and the like. Alkali metal salts of polystyrene sulfonic acid such as the sodium salt of polystyrene sulfonic acid is highly preferred, since the use of this polymer in the intermediate layer results in better anti-static properties of the receiving element. Anti-static coatings such as those described in EP 440,957 can be incorporated in the intermediate layer or in the subbing layer. This results both in a higher hydrophilicity and in better anti-static properties.

The intermediate layer may further comprise polymeric dispersions or latices, surfactants, inorganic particles such as silica and colloidal silica and the like. Addition of surfactants, colloidal silica and/or latices is preferred. Addition of silica to the intermediate layer decreases sticking to the coating roll after coating. Addition of latices to the intermediate layer improves the addition and improves the removing step in the recycling process in case of acrylic acid or methacrylic acid type latices.

The intermediate layer may also have a cushioning property, such as mentioned in US 4,734,397.

The support for the receiver sheet may be a transparent film of e.g. polyethylene terephthalate, a polyether sulfone, a polyimide, a cellulose ester, or a polyvinyl alcohol-co-acetal. The support may also be a reflective one such as baryta-coated paper, polyethylene-coated paper, or white polyester i.e. white-pigmented polyester. Blue-coloured polyethylene terephthalate film can also be used as a support.

Although the subbing layer is useful for application on polyethylene-coated paper, substrates based on polyester, transparent or reflective, are preferred. In this case, the subbing layer can be applied before, during or after the biaxial stretching procedure.

At the opposite side of the receiving element (opposite to the receiving layer), a backcoat can be provided, optionally in combination, with an appropriate subbing layer to improve the adhesion between the backcoat and the support.

Hydrophilic as well as hydrophobic backcoats can be used. Hydrophilic backcoats can be applied easily from water, while hydrophobic backcoats have the advantage that the backcoat performs well at all humidity levels (no curl).

Examples of hydrophilic backcoat layers are layers comprising polyvinylalcohol, polyethylene glycol, polyacrylamide, hydroxyethylcellulose, dextran and gelatin. The use of gelatin is highly preferred.

These hydrophilic backcoat layers may further comprise dispersions or latices of hydrophobic polymers, inorganic particles, surfactant and the like. The addition of these particles can be used in order to obtain a specific surface gloss, such as mentioned in EP-A 543 441. Especially preferred particles are silica and polymethylmethacrylate beads of 0.5 to 10 µm. Antistatic treatment can also be provided to said backcoat layer.

Examples of hydrophobic backcoat layers are backcoat layers comprising addition polymers such as polymethylmethacrylate, polyvinylchloride and polycondensates such as polyesters, polycarbonates in combination with the above mentioned particles for the hydrophilic backcoat layers.

With hydrophobic backcoat layers, it can be useful to provide an intermediate hydrophilic layer between the subbing layer and the backcoat layer, such as those mentioned for use at the receiving side of the receiving element, in order to improve the removal of the backcoat layer in the recycling procedure.

The printing method of the present invention uses a thermal head to selectively heat specific portions of the donor element in contact with a receiving element. The thermal head can be a thick or thin film thermal head although the use of a thin film thermal head is preferred, since this offers more opportunities to obtain appropriate gradation. The pressure applied to the thermal head is preferably between 120 and 400 g/cm heater line. A spatial resolution of 150 dpi or higher is preferred. The average printing power is calculated as the total amount of energy applied during one line time divided by the line time and by the surface area of the heat-generating elements.

Although a higher average printing power results in higher optical densities of the final image, it is preferred to use an average printing power below 10 W/mm2. At higher printing energies, deformation of the receiving layer and/or receiving sheet occurs.

The time needed for printing one single line with the thermal head, also called the line time, is preferably below 45 ms. Longer line times result in longer printing times and more deformation of the receiving sheet and/or receiving layer.

In order to increase the density of the final image after printing line-by-line with a thermal head, an overall heat treatment of the receiving element may be performed. This heat treatment can be e.g. done with an infrared source, a heated air stream or a hot plate but is preferably done by means of a heated roller.

It is believed that during the overall heat treatment, the transferred reducing agent can further react with the reducible silver source.

By selecting the appropriate diameter and speed of the heated roller, the heat treatment time for the overall heating can be adjusted. 'Moreover, the heated rollers can be used to uncurl the receiving sheet after printing.

The following examples illustrate the invention in more detail without, however, limiting the scope thereof.

EXAMPLES Preparation of the receiving element

A subbed polyethylene terephthalate support having a thickness of 100 µm was coated in order to obtain the following receiving layer : silver behenate 4.5 g/m2 compound II mentioned above 0.34 g/m2 polyvinylbutyral (Butvar B79, Monsanto) 4.5 g/m2

After drying, a release layer was coated from hexane comprising 0.03 g/m2 Tegoglide™ 410 (polyether-polysiloxane blockcopolymer from Goldschmidt). This receiving element was used in the following printing examples.

Preparation of the donor elements

Both sides of a 5.7 µm thick polyethylene terephthalate support were coated with a subbing layer of a copolyester comprising ethylene glycol, adipic acid, neopentyl glycol, terephthalatic acid, isophthalic acid, and glycerol.

The resulting subbing layer was covered with a solution in methyl ethyl ketone of 13% of a polycarbonate having the following structural formula (III):

wherein n represents the number of units to obtain a polycarbonate having a relative viscosity of 1.30 as measured in a 0.5% solution in dichloromethane, 0.5% of talc (Nippon Talc P3, Interorgana) and 0.5% of zinc stearate.

Finally, a top layer of polyether-modified polydimethylsiloxane (Tegoglide™ 410, Goldschmidt) was coated from a solution in isopropanol on the resulting heat-resistant polycarbonate layer.

The other side of the donor element was provided with a donor layer. The nature of the ingredients is mentioned in table I. The binder and reducing agent were casted at a concentration of 10 weight% in butanone. These coating solutions were applied at a wet thickness of 10 µm by means of a wire bar. The resulting layer was dried by evaporation of the solvent.

Printing of the combination of donor and receiving elements

Printing was performed by contacting the donor layer side of the donor element with the receiving layer of the receiving element, followed by heating by means of a thermal head. The thermal head was a thin film thermal head heated (pulse wise activation) at an average printing power of 5 Watt/mm2 and a line time of 18 ms, a duty cycle of 75 % and with a resolution of 300 dpi. The pressure applied between the thermal head and the rotating drum carrying the receiving and donor element was 160 g/cm heater line. After printing, the receiving element was separated from the donor element.

The printed image was a 16-step grey scale between data level 0 and 255 (8 bit). The data levels of the different steps were choosen equidistant with respect to the input data level in order to obtain the native sensitometry.

The comparitive monosheet was printed in direct contact with the thermal head, without the use of a donor element.

Overall heat treatment

All receiving elements were reheated on a hot plate of 118°C for 10 seconds.

Measurement of the optical density of the prints

The optical maximal densities of the prints were measured behind a visual filter in a Macbeth™ TR924 densitometer in the grey scale part corresponding to data level 255.

Determination of the number of visible grey tones.

The number of visible grey tones of the printed image after heat treatment was determined by counting the number of fields of the grey scale which have a visual different grey density than the other fields (including the density corresponding to data level 0). A high number indicates a soft or low gradation.

The results are listed in table 1. Exam. Binder type Reducing agent Optical density after Visible grey tones printing heat treatment 1 I 1 0.80 1.30 10 2 II 1 0.90 1.53 10 3 III 1 0.80 1.32 - 4 IV 1 0.89 1.45 10 6 I 2 - 2.24 10 7 II 3 0.13 0.39 12 8 I 4 1.00 1.59 9 9 I 5 0.68 1.31 12 10 I 6 1.72 1.99 10 11 IV 7 0.44 1.05 11 12 I 8 1.66 2.29 12 13 I 9 1.23 2.10 11 14 I 10 0.92 1.53 11 15 I 11 1.45 1.73 11 16 I 12 - 2.24 - 17 I 13 - 2.47 - 18 I 14 - 1.80 - 19 I 15 - 1.78 - 20 I 16 - 1.79 - 21 Comparative Monosheet 260 - 5

The comparative monosheet (21) was prepared by coating a subbed polyethylene terephthalate support having a thickness of 170 µm so as to obtain thereon after drying the following recording layer including : silver behenate 4.47 g/m2 polyvinyl butyral 2.24 g/m2 reducing agent S as defined hereinafter 0.85 g/m2 3,4-dihydro-2,4-dioxo-1,3,2H-benzoxazine 0.32 g/m2 silicone oil 0.02 g/m2
Reducing agent S is a polyhydroxy spiro-bis-indane, viz. 3,3,3',3'-tetramethyl-5,6,5',6'-tetrahydroxy-spiro-bis-indane.

After drying said recording layer was coated at 22° C at a wet coating thickness of 100 µm with the following coating composition for forming a protective layer. methyl ethyl ketone 94 g polycarbonate according to formula (III) 6 g Tegoglide 410 (Goldschmidt) 0.6 g
The thus coated layer was dried in an air current whereby a protective scratch-resistant layer was obtained. This monosheet can thus be used without a donor element.

Reducing agents :

1
3,4,5-tri-hydroxy-n.propylbenzoate
2
3,4-dihydroxy-ethylbenzoate
3
p-phenylsulfonamido-phenol
4
3,4,5-trihydroxy-ethylbenzoate
5
3,4,5-trihydroxy-n.octylbenzoate
6
7
8
4-methoxy-naphtol
9
1,2-dihydroxy-4-phenyl-benzene
10
3,4,5-trihydroxy-methylbenzoate
11
3,4-dihydroxybenzoic acid
12
3,4-dihydroxybenzaldehyde
13
n.propyl-3,4-dihydroxyphenyl-ketone
14
phenyl-(3,4-dihydroxyphenyl)-ketone
15
3,4-dihydroxy-n.butylbenzoate
16
3,4-dihydroxy-n.hexylbenzoate

Binders

  • I Luran™ 388S (polystyrene-co-acrylonitrile, BASF)
  • II Cellulose acetate propionate (PLFS™ 130, Celanese)
  • III Nitrocellulose type E510 (Wolf Walsrode)
  • IV Cellulose acetate butyrate (CAB 171 15, Eastman Kodak).

It is clear from table I that high optical densities can be achieved by the above printing method. It is also clearly demonstrated that the heat treatment after printing further increases the optical density. Moreover, when continuous tone grey scales were printed with the donor elements in combination with the receiving element of the present example in a printer using a thermal head, a smooth grey scale having a low gradation is obtained. The number of visible grey tones is higher than in the prior art system (monosheet).


Anspruch[de]
  1. Ein thermisches Bilderzeugungsverfahren, in dem (i) ein Donorelement, das auf einem Träger eine Donorschicht mit einem Bindemittel und einem wärmeübertragbaren Reduktionsmittel, das durch Erhitzung eine Silberquelle zu Metallsilber zu reduzieren vermag, enthält, und (ii) ein Empfangselement benutzt werden, das auf einem Träger eine Empfangsschicht mit einer Silberquelle enthält, die in Gegenwart eines Reduktionsmittels durch Erhitzung reduziert werden kann, wobei das thermische Bilderzeugungsverfahren folgende Stufen umfaßt :
    • das Anordnen der Donorschicht des Donorelements in schichtseitiger Beziehung zur Empfangsschicht des Empfangselements,
    • die bildmäßige Thermokopferhitzung einer so erhaltenen Anordnung, wodurch eine bestimmte Menge des wärmeübertragbaren Reduktionsmittels entsprechend der durch den Thermokopf zugelieferten Wärmemenge bildmäßig auf das Empfangselement übertragen wird,
    • die Abtrennung des Donorelements vom Empfangselement, und
    • die darauffolgende Gesamterhitzung des Empfangselements.
  2. Thermisches Bilderzeugungsverfahren nach Anspruch 1, dadurch gekennzeichnet, daß die thermisch reduzierbare Silberquelle ein organisches Silbersalz ist.
  3. Thermisches Bilderzeugungsverfahren nach Anspruch 2, dadurch gekennzeichnet, daß das organische Silbersalz Silberbehenat ist.
  4. Thermisches Bilderzeugungsverfahren nach irgendeinem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die die Silberquelle enthaltende Empfangsschicht des Empfangselements ferner ein Tönungsmittel enthält.
  5. Thermisches Bilderzeugungsverfahren nach irgendeinem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß das Empfangselement ferner ein Trennmittel in der Empfangsschicht oder in einer separaten Schicht auf der Empfangsschicht enthält.
  6. Thermisches Bilderzeugungsverfahren nach Anspruch 5, dadurch gekennzeichnet, daß als Trennmittel eine Silikon-verbindung benutzt wird.
  7. Thermisches Bilderzeugungsverfahren nach irgendeinem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß die mittlere Druckleistung des Thermokopfes während der bildmäßigen Erhitzung nicht mehr als 10 Watt/mm2 beträgt.
  8. Thermisches Bilderzeugungsverfahren nach irgendeinem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß die bildmäßige Erhitzung zeilenweise erfolgt und die für den Thermokopf zum Drucken einer einzelnen Zeile benötigte Zeit höchstens 45 ms beträgt.
  9. Thermisches Bilderzeugungsverfahren nach irgendeinem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß die Gesamterhitzung mittels einer erhitzten Walze erfolgt.
Anspruch[en]
  1. A thermal imaging process using (i) a donor element comprising on a support a donor layer containing a binder and a thermotransferable reducing agent capable of reducing a silver source to metallic silver upon heating and (ii) a receiving element comprising on a support a receiving layer comprising a silver source capable of being reduced by means of heat in the presence of a reducing agent, said thermal imaging process comprising the steps of
    • bringing said donor layer of said donor element into face to face relationship with said receiving layer of said receiving element,
    • image-wise heating a thus obtained assemblage by means of a thermal head, thereby causing image-wise transfer of an amount of said thermotransferable reducing agent to said receiving element in accordance with the amount of heat supplied by said thermal head,
    • separating said donor element from said receiving element, and
    • subsequent overall heating of said receiving element.
  2. A thermal imaging process according to claim 1, wherein said thermally reducible source of silver is an organic silver salt.
  3. A thermal imaging process according to claim 2, wherein said organic silver salt is silver behenate.
  4. A thermal imaging process according to any of claims 1 to 3, wherein said receiving layer of said receiving element containing said silver source further comprises a toning agent.
  5. A thermal imaging process according to any of claims 1 to 4, wherein said receiving element further comprises a release agent in said receiving layer or in a separate layer on top thereof.
  6. A thermal imaging process according to claim 5, wherein said release agent is a silicone compound.
  7. A thermal imaging process according to any of the preceding claims wherein the average printing power applied by means of the thermal head during said image-wise heating is not more than 10 Watt/mm2.
  8. A thermal imaging process according to any of claims 1 to 7, wherein said image-wise heating is carried out line by line and wherein the time for printing a single line with said thermal head is at most 45 ms.
  9. A thermal imaging process according to any of the preceding claims, wherein said overall heating is performed by means of a heated roller.
Anspruch[fr]
  1. Un procédé d'imagerie thermique utilisant (i) un élément donneur comprenant sur un support une couche donneuse contenant un liant et un agent réducteur thermotransférable qui est capable de réduire une source d'argent en argent métallique lors du chauffage et (ii) un élément récepteur comprenant sur un support une couche réceptrice comprenant une source d'argent qui est capable d'être réduite par la chaleur en présence d'un agent réducteur, ce procédé d'imagerie thermique comprenant les phases consistant à:
    • amener la couche donneuse de l'élément donneur en relation de face à face avec la couche réceptrice de l'élément récepteur,
    • chauffer en forme d'image un assemblage ainsi obtenu au moyen d'une tête thermique pour faire ainsi en sorte de transférer en forme d'image une quantité de l'agent réducteur thermotransférable à l'élément récepteur en fonction de la quantité de chaleur fournie par ladite tête thermique,
    • séparer l'élément donneur de l'élément récepteur, et
    • chauffer ensuite globalement l'élément récepteur.
  2. Un procédé d'imagerie thermique selon la revendication 1, caractérisé en ce que la source d'argent thermoréductible est un sel d'argent organique.
  3. Un procédé d'imagerie thermique selon la revendication 2, caractérisé en ce que le sel d'argent organique est du béhénate d'argent.
  4. Un procédé d'imagerie thermique selon l'une quelconque des revendications 1 à 3, caractérisé en ce que la couche réceptrice dudit élément récepteur contenant ladite source d'argent comprend en plus un agent influençant le ton d'image.
  5. Un procédé d'imagerie thermique selon l'une quelconque des revendications 1 à 4, caractérisé en ce que ledit élément récepteur comprend en plus un agent de séparation dans ladite couche réceptrice ou dans une couche séparée située au-dessus d'elle.
  6. Un procédé d'imagerie thermique selon la revendication 5, caractérisé en ce que l'agent de séparation est un composé de silicone.
  7. Un procédé d'imagerie thermique selon l'une quelconque des revendications précédentes, caractérisé en ce que la puissance d'impression moyenne appliquée au moyen de la tête thermique pendant le chauffage en forme d'image n'excède pas 10 Watt/mm2
  8. Un procédé d'imagerie thermique selon l'une quelconque des revendications 1 à 7, caractérisé en ce que le chauffage en forme d'image s'effectue ligne par ligne et que le temps pour imprimer une seule ligne avec la tête thermique est au maximum 45 ms.
  9. Un procédé d'imagerie thermique selon l'une quelconque des revendications précédentes, caractérisé en ce que le chauffage global s'effectue au moyen d'un rouleau chauffé.






IPC
A Täglicher Lebensbedarf
B Arbeitsverfahren; Transportieren
C Chemie; Hüttenwesen
D Textilien; Papier
E Bauwesen; Erdbohren; Bergbau
F Maschinenbau; Beleuchtung; Heizung; Waffen; Sprengen
G Physik
H Elektrotechnik

Anmelder
Datum

Patentrecherche

Patent Zeichnungen (PDF)

Copyright © 2008 Patent-De Alle Rechte vorbehalten. eMail: info@patent-de.com